Slabs of natural stone for external paving EN 1341 and EN 1342
Trade Name | QUARTZITE ELDORADA | |||
Country of Provenance | Sao Tomé, Minas Gerais - BRAZIL - | |||
Type of Test | Standard | Units | Conditioning | Average |
Petrographic examination | EN 12407:2007 | Quartzite | ||
Water absorption at atmospheric pressure | EN 13755:2008 | % | - | 0.1 |
Flexural strength under concentrated load | EN 12372:2007 | MPa | Dry | 22.8 |
After No. 56 Freeze/Thaw cycles | 22,2 | |||
Frost resistant | Yes | |||
Compressive strength | EN 1926:2007 | MPa | Dry | 235.0 |
After No. 56 Freeze/Thaw cycles | 201.7 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 65 |
Resistance to abrasion | EN 14157:2005 | mm. | - | 14.5 |
Trade Name | QUARTZITE ELDORADA PINK | |||
Country of Provenance | Sao Tomé, Minas Gerais - BRAZIL - | |||
Type of Test | Standard | Units | Conditioning | Average |
Petrographic examination | EN 12407:2007 | Quartzite | ||
Water absorption at atmospheric pressure | EN 13755:2008 | % | - | 0.1 |
Flexural strength under concentrated load | EN 12372:2007 | MPa | Dry | 16.2 |
After No. 56 Freeze/Thaw cycles | 15.5 | |||
Frost resistant | Yes | |||
Compressive strength | EN 1926:2007 | MPa | Dry | 280.0 |
After No. 56 Freeze/Thaw cycles | 251.3 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 62 |
Resistance to abrasion | EN 14157:2005 | mm. | - | 16 |
Trade Name | QUARTZITE EUROPA GREY | |||
Country of Provenance | Kavala - GREECE | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Quartzite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.45 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 27.49 |
After No. 48 Freeze/Thaw cycle | 25.87 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 22.67 |
After No. 48 Freeze/Thaw cycle | 19.48 | |||
Frost resistant | Yes - F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 58 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 48 |
Trade Name | QUARTZITE GOLDEN YELLOW | |||
Country of Provenance | Fangshan, Beijing - CHINA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Marble | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.12 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 14.93 |
After No. 48 Freeze/Thaw cycle | 14.36 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 10.18 |
After No. 48 Freeze/Thaw cycle | 7.16 | |||
Frost resistant | Yes - F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 73 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 68 |
Trade Name | QUARTZITE GREY | |||
Country of Provenance | Fangshan, Beijing - CHINA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Marble | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.15 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 19.60 |
After No. 48 Freeze/Thaw cycle | 17.82 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 13.58 |
After No. 48 Freeze/Thaw cycle | 13.63 | |||
Frost resistant | Yes - F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 60 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 52 |
Trade Name | QUARTZITE HONEY | |||
Country of Provenance | - TURKEY - | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Marble | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.15 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 20.92 |
After No. 48 Freeze/Thaw cycle | 19.99 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 14.42 |
After No. 48 Freeze/Thaw cycle | 11.11 | |||
Frost resistant | Yes - F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 60 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 55 |
Trade Name | MODAK YELLOW | |||
Country of Provenance | Gwalior - Madhya - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Quartzite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 1.89 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 19.16 |
After No. 48 Freeze/Thaw cycle | 17.39 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 12.95 |
After No. 48 Freeze/Thaw cycle | 12.38 | |||
Frost resistant | Yes - F1 | |||
Compressive strength | EN 1926:1999 | MPa | Dry | 36.74 |
After No. 48 Freeze/Thaw cycle | 58.66 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 81 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex | USRV | - | 73 |
Trade Name | MINT | |||
Country of Provenance | Gwalior - Madhya - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Meta-quartzarenite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 3.62 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 11.89 |
After No. 48 Freeze/Thaw cycle | 13.32 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 10.66 |
After No. 48 Freeze/Thaw cycle | 10.79 | |||
Frost resistant | Yes - F1 | |||
Compressive strength | EN 1926:1999 | MPa | Dry | 40.09 |
After No. 48 Freeze/Thaw cycle | 37.26 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 84 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 82 |
Trade Name | GREY SLATE | |||
Country of Provenance | Papagaios - Minas Gerais - BRAZIL - | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.32 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 54.01 |
After No. 48 Freeze/Thaw cycle | 9.97 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 35.66 |
After No. 48 Freeze/Thaw cycle | 6.74 | |||
Frost resistant | No - F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 42 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 35 |
Trade Name | MULTICOLOUR SLATE | |||
Country of Provenance | Papagaois - Minas Gerais - BRAZIL - | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.54 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 39.68 |
After No. 48 Freeze/Thaw cycle | 12.56 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 24.21 |
After No. 48 Freeze/Thaw cycle | 7.80 | |||
Frost resistant | No - F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 57 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 47 |
Trade Name | BLACK SLATE | |||
Country of Provenance | Pintagui - Minas Gerais - BRAZIL | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.36 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 50.14 |
After No. 48 Freeze/Thaw cycle | 11.74 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 37.89 |
After No. 48 Freeze/Thaw cycle | 9.69 | |||
Frost resistant | No - F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 38 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 36 |
Trade Name | GREEN SLATE | |||
Country of Provenance | Felixlandia - Minas Gerais - BRAZIL | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.56 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 34.77 |
After No. 48 Freeze/Thaw cycle | 16.27 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 22.68 |
After No. 48 Freeze/Thaw cycle | 9.05 | |||
Frost resistant | No - F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 49 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 39 |
Trade Name | PURPLE SLATE | |||
Country of Provenance | Felixlandia - Minas Gerais - BRAZIL | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.37 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 51.05 |
After No. 48 Freeze/Thaw cycle | 10.90 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 37.65 |
After No. 48 Freeze/Thaw cycle | 7.38 | |||
Frost resistant | No - F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 53 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 43 |
Trade Name | DOLPHUR | |||
Country of Provenance | Karoli Discrict - Rajasthan - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Meta-quartzarenite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 2.63 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 13.93 |
After No. 48 Freeze/Thaw cycle | 12.17 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 7.82 |
After No. 48 Freeze/Thaw cycle | 8.87 | |||
Frost resistant | Yes – F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 80 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 63 |
Trade Name | INDIA GIALLA | |||
Country of Provenance | Lalitpur Discrict - Uttar Pradesh - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Meta-quartzarenite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 2.26 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 21.21 |
After No. 48 Freeze/Thaw cycle | 20.19 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 13.96 |
After No. 48 Freeze/Thaw cycle | 14.93 | |||
Frost resistant | Yes – F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 83 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 76 |
Trade Name | INDIA GRIGIA | |||
Country of Provenance | Kota and Bundi Discrict - Rajasthan - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Meta-quartzarenite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.89 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 28.24 |
After No. 48 Freeze/Thaw cycle | 28.34 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 20.81 |
After No. 48 Freeze/Thaw cycle | 19.26 | |||
Frost resistant | Yes – F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 77 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 72 |
Trade Name | MULTICOLOUR PEACOCK | |||
Country of Provenance | Kund Haryana - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Slate | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 2.40 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 33.92 |
After No. 48 Freeze/Thaw cycle | 23.25 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 8.92 |
After No. 48 Freeze/Thaw cycle | 10.89 | |||
Frost resistant | No – F0 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 57 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 45 |
Trade Name | SILVER GREY | |||
Country of Provenance | Bhilwara - Rajasthan - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Schist | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.17 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 39.42 |
After No. 48 Freeze/Thaw cycle | 37.10 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 30.14 |
After No. 48 Freeze/Thaw cycle | 27.35 | |||
Frost resistant | Yes – F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 54 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 36 |
Trade Name | RAINBOW | |||
Country of Provenance | Makrana -Rajasthan - INDIA | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Meta-quartzarenite | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 4.94 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 10.95 |
After No. 48 Freeze/Thaw cycle | 9.45 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 9.49 |
After No. 48 Freeze/Thaw cycle | 8.00 | |||
Frost resistant | Yes – F1 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 77 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 74 |
Trade Name | STONE OF LUSERNA GREY | |||
Country of Provenance | Montoso, Bagnolo Piemonte - Cuneo - ITALY | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Gneiss | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.31 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 19.96 |
After No. 48 Freeze/Thaw cycle | 19.54 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 17.20 |
After No. 48 Freeze/Thaw cycle | 17.65 | |||
Frost resistant | Yes - F1 | |||
Compressive strength | EN 1926:1999 | MPa | Dry | 116.08 |
After No. 48 Freeze/Thaw cycle | 103.51 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 69 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 67
|
Trade Name | STONE OF LUSERNA YELLOW | |||
Country of Provenance | Montoso, Bagnolo Piemonte - Cuneo - ITALY | |||
Type of Test | European | Units | Conditioning | Average |
Petrographic examination | EN 12407:2000 | Gneiss | ||
Water absorption at atmospheric pressure | EN 13755:2001 | % | - | 0.32 |
Flexural strength under concentrated load | EN 12372:1999 | MPa | Dry | 18.97 |
After No. 48 Freeze/Thaw cycle | 18.42 | |||
Flexural strength under concentrated load, minimum expected value to be indicated in the CE marking. | EN 12372:1999 | MPa | Dry | 13.98 |
After No. 48 Freeze/Thaw cycle | 15.69 | |||
Frost resistant | Yes - F1 | |||
Compressive strength | EN 1926:1999 | MPa | Dry | 84.69 |
After No. 48 Freeze/Thaw cycle | 77.47 | |||
Measurement of unpolished slip resistance value | Annex D | USRV | - | 69 |
Measurement of unpolished slip resistance value, minimum expected value to be indicated in the CE marking | Annex D | USRV | - | 64 |